Opis

Nitinol is a shape memory alloy (SMA) capable of martensite-to-austenite phase transformations enabling shape-memory behavior. Shape-memory properties make Nitinol a strong candidate material for use in aircraft applications such as actuators. Structural integrity and reliability of torque tube actuators must be assured before this material can be used in flight-critical components. Thorough understanding of the fatigue response of the material is essential for a structurally-sound SMA actuator design. The present effort investigates pure torsion and combined tension-torsion fatigue behavior of Nitinol at room temperature. Monotonic tests in tension and torsion were conducted to typify uni-directional stress-strain behavior. Fully-reversed torsion fatigue tests were conducted with shear stress ranges of 416, 584, 674, and 1310 MPa. In fully-reversed biaxial fatigue tests, a shear stress range of 500 MPa was superimposed on the axial stress ranges of 250, 500, 1000, 1120, and 1500 MPa. Fatigue behavioral characteristics, including fatigue S-N curves were established. Fatigue lives obtained in torsion-dominated biaxial tests were similar to those obtained in pure torsion. Conversely, tension-dominated biaxial fatigue was significantly more damaging, resulting in decreased fatigue lives. Applicability of von Mises criterion to correlating uniaxial and biaxial test results was examined. Evolution of stress-strain behavior with cycling is discussed.

Szczegóły książki

Kategoria Knihy po anglicky Society & social sciences Education

• Pełny tytuł: Biaxial Fatigue Behavior of Niti Shape Memory Alloy
• Autor: Daniel M Jensen
• Język: Angielski
• Oprawa: Miękka
• Liczba stron: 104
• EAN: 9781288405763
• ISBN: 9781288405763
• ID: 08250228
• Wydawca: Biblioscholar
• Waga: 200 g
• Wymiary: 246 × 189 × 6 mm
• Data wydania: 05. December 2012

Ulubione w innej kategorii

---

---

---